6VX19+FC Steel Wire Rope

a. Wires: steel wires for wire ropes are normally made of non-alloy carbon steel with a carbon content of 0.4 to 0.95%. The tensile forces and to run over sheaves with relatively small diameters.
b. Strand: the strand is a component of wire rope usually consisting of an assembly of wires of appropriate diamsions laid helically in one or more layers around a central element.
c. Core: the core is the central element, of fiber or steel, around which are laid helically the outer strands of wire rope. The core provides proper support for the strands under normal bending and loading conditions.
d. Wire rope is several strands of metal wire twisted into a helix forming a composite "rope", in a pattern known as "laid rope". Larger diameter wire rope consists of multiple strands.

Mine hoisting, blast furnace hoisting, large casting, oil drilling, forestry and marine industries,all kinds ofelevator, large hoisting, ground cable car ships and offshore facilities, cable railing.

Diameter MM	Approx.Weight			Minimun Breaking Load of Rope（KN)
	Kg/100m			1570Mpa		1670Mpa
	NF	SF	IWR	FC	IWR	FC	IWR
20	165	162	175	236	250	250	266
22	199	196	212	285	302	303	322
24	237	233	252	339	360	361	383
26	279	273	295	398	422	423	449
28	323	317	343	462	490	491	521
30	371	364	393	530	562	564	598
32	422	414	447	603	640	641	681
34	476	467	505	681	722	724	768
36	534	524	566	763	810	812	861

Diameter MM	Approx.Weight			Minimun Breaking Load of Rope（KN)
	Kg/100m			1770Mpa		1870Mpa		1960Mpa
	NF	SF	IWR	FC	IWR	FC	IWR	FC	IWR
20	165	162	175	266	282	280	298	294	312
22	199	196	212	321	341	339	360	356	378
24	237	233	252	382	406	404	429	423	449
26	279	273	295	449	476	474	503	497	527
28	323	317	343	520	552	550	583	576	612
30	371	364	393	597	634	631	670	662	702
32	422	414	447	680	721	718	762	753	799
34	476	467	505	767	814	811	860	850	902
36	534	524	566	860	913	909	965	953	1010

1.stainless steel :
providing good corrosion resistance and strength comparable to galvanized carbon steel grades.
2.galvanized steel:
Zinc coated carbon steel offers some corrosion resistance. It remains ductile over long periods of working. Usually higher break strengths than stainless steels.