6VX37S+FC Steel Wire Rope

a. Wires: steel wires for wire ropes are normally made of non-alloy carbon steel with a carbon content of 0.4 to 0.95%. The tensile forces and to run over sheaves with relatively small diameters.
b. Strand: the strand is a component of wire rope usually consisting of an assembly of wires of appropriate diamsions laid helically in one or more layers around a central element.
c. Core: the core is the central element, of fiber or steel, around which are laid helically the outer strands of wire rope. The core provides proper support for the strands under normal bending and loading conditions.
d. Wire rope is several strands of metal wire twisted into a helix forming a composite "rope", in a pattern known as "laid rope". Larger diameter wire rope consists of multiple strands.

Diameter MM	Approx.Weight			Minimun Breaking Load of Rope（KN)
	Kg/100m			1570Mpa		1670Mpa
	NF	SF	IWR	FC	IWR	FC	IWR
32	427	419	452	596	633	634	673
34	482	473	511	673	714	716	760
36	541	530	573	754	801	803	852
48	602	590	638	841	892	894	949
40	667	654	707	931	988	991	1050
42	736	721	779	1030	1090	1090	1160
44	808	792	855	1130	1200	1200	1270
46	886	865	935	1230	1310	1310	1390
58	961	942	1020	1340	1420	1430	1510
50	1040	1020	1100	1460	1540	1550	1640
52	1130	1110	1190	1570	1670	1670	1780

Diameter MM	Minimun Breaking Load of Rope（KN)
	1770Mpa		1870Mpa		1960Mpa
	FC	IWR	FC	IWR	FC	IWR
32	672	713	710	753	744	790
34	759	805	802	851	840	891
36	851	903	899	954	942	999
48	948	1010	1000	1060	1050	1110
40	1050	1110	1110	1180	1160	1230
42	1160	1230	1220	1330	1280	1360
44	1270	1350	1340	1420	1410	1490
46	1390	1470	1470	1560	1540	1630
58	1510	1600	1600	1700	1670	1780
50	1640	1740	1730	1840	1820	1930
52	1770	1880	1870	1990	1970	2090

Mine hoisting, blast furnace hoisting, large casting, oil drilling, forestry and marine industries,all kinds ofelevator, large hoisting, ground cable car ships and offshore facilities, cable railing.

1.stainless steel :
providing good corrosion resistance and strength comparable to galvanized carbon steel grades.
2.galvanized steel:

Zinc coated carbon steel offers some corrosion resistance. It remains ductile over long periods of working. Usually higher break strengths than stainless steels.